Color stability evaluation of micro hybrid composite resins submitted to accelerated artificial aging

Gisseli Bertozzi Ávila, Sérgio Candido Dias, Mariana Lima da Costa Valente, José Augusto Marcondes Agnelli, Andréa Cândido dos Reis

Abstract


Objective: The aesthetics of dental materials is extremely important for the success of oral rehabilitation. Thus, in the present study we evaluated the color stability and the surface degradation of three micro hybrid composite resins after accelerated artificial aging process (AAA). Methods: Were prepared 24 specimens (n=8) for each material: Solidex, Artglass and Cesead, dimensions of Ø 15 mm by 2 mm in thickness. The samples were subjected to color analysis, before and after AAA, in a spectrophotometer according to the CIE L*a*b* parameters, and a sample of each material, was selected for morphological evaluation under scanning electron microscopy (SEM). The data were submitted to one-way ANOVA and Tukey test (α=0.05). Results: Artglass showed higher stability regarding the presence of red and yellow (p<0.05) when subjected to the AAA and fewer of these pigments (p<0.05) when compared to the Cesead and Solidex, which showed the highest luminance stability (p<0.05). ΔE Cesead was the most unstable (p<0.05). All resins analyzed by SEM showed superficial degradation when submitted to the AAA, mainly in resin Cesead. Conclusion: All materials analyzed demonstrate color change and surface degradation, Cesead resin showed the worse results.


Keywords


Accelerated Artificial Aging; Color Stability; Composite Resin; Dental Esthetic; Morphological.

Full Text:

PDF


DOI: http://dx.doi.org/10.11606/issn.2357-8041.clrd.2015.128882

Article Metrics

Metrics Loading ...

Metrics powered by PLOS ALM

Refbacks

  • There are currently no refbacks.




Copyright (c) 2017 Gisseli Bertozzi Ávila, Sergio Candido Dias, Mariana Lima da Costa Valente, José Augusto Marcondes Agnelli, Andréa Candido dos Reis

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.