Porosity, residual monomer and water sorption of conventional heat-cured, microwave-cured and cross-linked acrylic resins

Authors

  • Rodrigo Elias de Oliveira Laboratory of Human Evolutionary Studies, Department of Genetics and Evolutionary Biology, Institute of Biosciences, University of São Paulo, São Paulo, SP
  • Fernando Neves Nogueira Department of Biomaterials and Oral Biology, School of Dentistry, University of São Paulo, São Paulo, SP
  • Beatriz Silva Câmara Mattos Department of Maxillofacial Surgery, Prothesis and Traumatology, School of Dentistry, University of São Paulo, São Paulo, SP

DOI:

https://doi.org/10.11606/issn.2357-8041.clrd.2014.68723

Keywords:

Acrylic Resins, Dental Materials, Chemical Properties, Ocular Prosthesis, Porosity.

Abstract

This study compared the residual monomer release, water sorption and superfi cial porosity of different resins commonly employed in eye prostheses: heat-cured (HC); microwave-cured (MC) and self-curing cross-linked acrylic resins (SC). Four groups were established: G1, HC / water bath cycle; G2, MC / microwave cycle; G3, HC / microwave cycle; G4, SC. The amount of residual monomer was similar in G1 and G3, lower in G2 and higher in G4. Water sorption was similar in all groups. G2 showed more superfi cial porosity, and G1 and G3 were similar in this regard. Neither the conventional heat-curing cycle nor the microwave cycle affected the amount of residual monomer or porosity of the conventional heat-cured acrylic resin. Water sorption was not affected by the type of resin or polymerization cycle used. Residual monomer release and porosity were related to the type of resin employed rather than the polymerization cycle they were submitted to.

Downloads

Download data is not yet available.

References

Chalian V, Drane J, Standish S. Maxillofacial Prosthetics - multidisciplinary practice. Baltimore: The Williams & Wilkins; 1972.

Fountain TR, Goldberger S, Murphree AL. Orbital development after enucleation in early childhood. Ophthal Plast Reconstr Surg. 1999 Jan;15(1):32-6. 3. Gaia BF, Cheng CK, Perrone LJ, Rose MC, Mattos BS. Study of dimensional alterations of the orbit following loss of the eye. Int J Prosthodont. 2006 May-Jun;19(3):264-5.

Coas VR, Neves AC, Rode SM. Evaluation of the etiology of ocular globe atrophy or loss. Braz Dent J. 2005;16(3):243-6. doi: 10.1590/S0103-64402005000300013.

Mattos BSC, Montagna MC, Fernandes CS, Saboia AC. The pediatric patient at a maxillofacial service: Eye prosthesis. Braz Oral Res. 2006 Jul-Sep;20(3):247-51. doi: 10.1590/S1806-83242006000300012.

Bastiaan RJ. Denture estomatitis. In: Smith DC, Williams DF. Biocompatibility of dental materials. Boca Raton: CRC Press; 1982.

Manikantan NS, Ahila SC, Manojkumar AD. Cytotoxicity of acrylic denture base resins. KDJ (Kerala Dental Journal). 2011 Mar;34(1 Suppl):105-6.

Çelebi N, Yüzügüllü B, Canay S, Yücel U. Effect of polymerization methods on the residual monomer level of acrylic resin denture base polymers. Polym Adv Technol. 2008 Mar;19(3):201-6. doi: 10.1002/pat.996.

Kanerva L, Jolanki R, Estlander T. 10 years of patch testing with the (meth)acrylate series. Contact Dermatitis. 1997 Dec;37(6):255-8. doi: 10.1111/j.1600-0536.1997.tb02460.x.

Verran J, Maryan CJ. Retention of Candida albicans on acrylic resin and silicone of different surface topography. J Prosthet Dent. 1997 May;77(5):535-9. doi: 10.1016/S0022-3913(97)70148-3.

Radford DR, Sweet SP, Challacombe SJ, Walter JD. Adherence of Candida albicans to denture-base materials with different surface finishes. J Dent. 1998 Sep;26(7):577-83. doi:10.1016/S0300-5712(97)00034-1.

Radford DR, Challacombe SJ, Walter JD. Denture plaque and adherence of Candida albicans to denture-base materials in vivo and in vitro. Crit Rev Oral Biol Med. 1999;10(1):99-116.

Salim N, Satterthwaite JD, Rautemaa R, Silikas N. Impregnation with antimicrobials challenge bonding properties and water sorption behaviour of an acrylic liner. J Dent. 2012 Aug;40(8):693-9. doi: 10.1016/j.jdent.2012.04.027.

Anusavice KJ. Phillips Materiais dentários. 10a ed. Rio de Janeiro: Guanabara Koogan; 1998.

Aldoori D, Huggett R, Bates JF, Brooks SC. A Comparison of Denture Base Acrylic Resins Polymerized by Microwave

Irradiation and by Conventional Water Bath Curing Systems. Dent Mater. 1988 Feb;4(1):25-32. doi:10.1016/S0109-

(88)80084-8.

Blagojevic V, Murphy VM. Microwave polymerization of denture base materials. A comparative study. J Oral Rehabil. 1999

Oct;26(10):804-8. doi: 10.1046/j.1365-2842.1999.00456.x

De Clerck JP. Microwave polymerization of acrylic resins used in dental prostheses. J Prosthet Dent. 1987 May;57(5):650-8.

doi:10.1016/0022-3913(87)90353-2.

Reitz PV, Sanders JL, Levin B. The curing of denture acrylic resins by microwave energy. Physical properties. Quintessence

Int. 1985 Aug;16(8):547-51.

Lamb DJ, Ellis B, Priestley D. Loss into water of residual monomer from autopolymerizing dental acrylic resin.

Biomaterials. 1982 Jul;3(3):155-9. doi:10.1016/0142-9612(82)90005-9.

Del Bel Cury A A, Rached RN, Ganzarolli SM. Microwave-cured acrylic resins and silicone-gypsum moulding technique. J Oral Rehabil. 2001 May; 28(5):433-8. doi: 10.1046/j.1365-2842.2001.00684.x.

Tuna SH, Keyf F, Gumus HO, Uzun C. The Evaluation of Water Sorption/Solubility on Various Acrylic Resins. Eur J Dent.

Jul;2(3):191-7.

Phoenix RD. Resinas para Base de Prótese Total. In: Anusavice KJ. Phillips Materiais dentários. 11a ed. Rio de Janeiro:

Elsevier; 2005.

Paes-Junior TJA, Carvalho RF, Cavalcanti SCM, Saavedra GSFA, Borges ALS. Influence of plaster drying on the amount

of residual monomer in heat-cured acrylic resins. Braz J Oral Sci. 2013 Abr-Jun;12(2):84-9.

Ilbay SG, Guvener S, Alkumru HN. Processing dentures using a microwave technique. J Oral Rehabil. 1994 Jan;21(1):103-9.

doi:10.1111/j.1365-2842.1994.tb01129.x.

Revised American Dental Association specification no. 12 for denture base polymers. J Am Dent Assoc. 1975 Feb;90(2):451-8.

Arima T, Murata H, Hamada T. Properties of highly crosslinked autopolymerizing reline acrylic resins. J Prosthet Dent. 1995 Jan;73(1):55-9.

Pfeiffer P, Rosenbauer EU. Residual methyl methacrylate monomer, water sorption, and water solubility of hypoallergenic

denture base materials. J Prosthet Dent. 2004 Jul;92(1):72-8. doi:10.1016/S0022391304002057.

Compagnoni MA, Barbosa DB, de Souza RF, Pero AC. The effect of polymerization cycles on porosity of microwaveprocessed

denture base resin. J Prosthet Dent. 2004 Mar;91(3):281-5. doi:10.1016/S0022391304000083.

Levin B, Sanders JL, Reitz PV. The use of microwave energy for processing acrylic resins. J Prosthet Dent. 1989

Mar;61(3):381-3. doi:10.1016/0022-3913(89)90150-9.

Alkhatib MB, Goodacre CJ, Swartz ML, Munoz-Viveros CA, Andres CJ. Comparison of microwave-polymerized denture

base resins. Int J Prosthodont. 1990 May-Jun;3(3):249-55.

Rizzatti-Barbosa CM, Ribeiro-Dasilva MC. Inf luence of Double Flask Investing and Microwave Heating on the Superficial

Porosity, Surface Roughness, and Knoop Hardness of Acrylic Resin. J Prosthodont. 2009 Aug;18(6):503-6. doi:

1111/j.1532-849X.2009.00469.x.

Oliveira VM, Leon BL, Del Bel Cury AA, Consani S. Influence of number and position of flasks in the monomer release,

Knoop hardness and porosity of a microwave-cured acrylic resin. J Oral Rehabil. 2003 Nov;30(11):1104-8. doi:

1046/j.1365-2842.2003.01195.x

Botega DM, de Souza Machado T, de Mello JA, Garcia RC, Del Bel Cury AA. Polymerization time for a microwave-cured

acrylic resin with multiple flasks. Braz Oral Res. 2004 Jan-Mar;18(1):23-8.

Ganzarolli SM, Nunes de Mello JA, Shinkai RS, Del Bel Cury AA. Internal adaptation and some physical properties

of methacrylate-based denture base resins polymerized by different techniques. J Biomed Mater Res B: Appl Biomater.

Jul;82(1):169-73. doi: 10.1002/jbm.b.30718.

Yannikakis S, Zissis A, Polyzois G, Andreopoulos A. Evaluation of porosity in microwave-processed acrylic resin using a

photographic method. J Prosthet Dent. 2002 Jun;87(6):13-9. doi: 10.1067/mpr.2002.124490.

Downloads

Published

2014-09-28

Issue

Section

Original Research

How to Cite

Oliveira, R. E. de, Nogueira, F. N., & Mattos, B. S. C. (2014). Porosity, residual monomer and water sorption of conventional heat-cured, microwave-cured and cross-linked acrylic resins. Clinical and Laboratorial Research in Dentistry, 20(3), 137-144. https://doi.org/10.11606/issn.2357-8041.clrd.2014.68723